Structural and physical properties of sm-doped Bi1.6Pb0.4Sr2Ca2-xSmxCu3Oy superconductors
Yükleniyor...
Dosyalar
Tarih
2005
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Elsevier Science Bv
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
The superconducting Bi1.6Pb0.4Sr2Ca2-xSMxCu3Oy (X = 0.0, 0.0005, 0.001, 0.005, 0.01, 0.1, 0.5, 1.0, and 1.5) system was investigated for different concentrations of Sm. The structural analysis was carried out by XRD. XRD results show that the samples with substitution of various amounts of Sm for Ca transform from the major high-T-c phase (Bi-2223) to the low-T-c phase (Bi-2212). The lattice parameter data extracted from XRD showed that with increasing Sm concentration (x), the lattice parameter a increases slightly while the lattice parameter c decreases significantly. DC resistivity measurements were carried out by the standard four-probe technique in the temperature range between 25 K and 130 K. With increasing Sm substitution up to x = 0.1, the values of T-e(offset) vary between 107 K and 70 K. The samples with x > 0.1 did not show any superconducting transition down to 25 K. The critical current density measurements were performed in liquid nitrogen. Critical current density decreases with increasing Sm substitution, and it was measured to be 43 A/cm(2) for the sample with x = 0.0 at zero field. Microstructure examinations were carried out by SEM. All the reported data were discussed, and compared with earlier results on Sm and other substituted Bi-Sr-Ca-Cu-O system.
Açıklama
Anahtar Kelimeler
Bi-based Cuprates, Transport Properties, Doping and Substitution, Critical Currents, Transition Temperature Variations
Kaynak
Physica C-Superconductivity And Its Applications
WoS Q Değeri
Q3
Scopus Q Değeri
Q2
Cilt
423
Sayı
3-4