Effect of magnetic field direction on magnetoresistivity, activation energy, irreversibility and upper critical field of Bi-2212 thin film fabricated by DC sputtering method
Yükleniyor...
Dosyalar
Tarih
2012
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Springer
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
This study aims to investigate the effect of magnetic field direction on superconducting properties of Bi-2212 thin film fabricated on MgO (100) substrate using the direct current (DC) magnetron reactive sputtering technique at 100 watt with the aid of magnetoresistivity measurements. The zero resistivity transition temperatures (T-c), irreversibility fields (mu H-0(irr)) and upper critical fields (mu H-0(c2)) are deduced from the magnetoresistivity versus temperature curves under DC magnetic fields (parallel and perpendicular to c-axis) up to 5 T. Moreover, thermally activated flux flow (TAFF) model is studied for activation energy (U-0) values of the sample. It is found that the T-c value decreases from 76.4 K to 39.1 K for the applied magnetic field perpendicular to c-axis (mu H-0 perpendicular to c-axis); likewise, the T-c reduces towards 28.8 K with the increase in the applied field parallel to c-axis (mu H-0 parallel to c-axis). Furthermore, the U-0 values are found to decrease considerably with increasing applied magnetic field. In fact, the U-0 of 134.5 K is obtained to be smallest at 5 T field parallel to the c-axis. Additionally, both the mu H-0(irr) and mu H-0(c2) values determined are also observed to reduce with the increase of the applied magnetic field. At absolute zero temperature (T = 0 K), the extrapolation of the mu H-0(irr)(T) and mu H-0(c2)(T) curves is used to obtain the mu H-0(irr)(0) and mu H-0(c2)(0) values of the film, respectively. The inner is found to be about 22.216 T (19.046 T) for the applied field perpendicular (parallel) to c-axis whereas the latter is determined to be about 54.095 T (126.522 T) for the applied field parallel (perpendicular) to c-axis, respectively, as a result of anisotropic behavior of the film prepared. On the other hand, penetration depths (lambda) and coherence lengths (xi) inferred from mu H-0(irr)(0) and mu H-0(c2)(0) values are obtained to be about 38.519 angstrom (41.601 angstrom) and 16.147 angstrom (24.685 angstrom) in the case of applied field perpendicular (parallel) to c-axis, respectively. Based on all the results, the change of the superconducting properties as a function of the magnetic field direction presents the anisotropy of the sample produced. X-ray diffraction (XRD) and scanning electron microscopy (SEM) examinations are also conducted for microstructural and phase analyses of the film.
Açıklama
Anahtar Kelimeler
Bi-2212 Thin Film, Magnetoresistivity, TAFF Model, Activation Energy, Irreversibility Field, Upper Critical Field
Kaynak
Journal Of Superconductivity And Novel Magnetism
WoS Q Değeri
Q4
Scopus Q Değeri
Q3
Cilt
25
Sayı
6