Significant development on pinning of vortices in Y-123 superconductor with homovalent Ba/Nd substitution

Basit Öğe Kaydı
dc.authorid0000-0002-0759-0598en_US
dc.authorid0000-0002-5177-3703en_US
dc.authorid0000-0002-3944-0367en_US
dc.authorid0000-0003-0049-0161
dc.authorid0000-0002-2969-0039
dc.contributor.authorSarıtekin, Namık Kemal
dc.contributor.authorÖz, Muhammed
dc.contributor.authorTerzioğlu, Cabir
dc.contributor.authorGörür, Osman
dc.contributor.authorYıldırım, Gürcan
dc.date.accessioned2021-06-23T19:43:25Z
dc.date.available2021-06-23T19:43:25Z
dc.date.issued2016
dc.departmentBAİBÜ, Fen Edebiyat Fakültesi, Fizik Bölümüen_US
dc.departmentBAİBÜ, Gerede Meslek Yüksekokulu, Kimya Ve Kimyasal İşleme Teknolojileri Bölümü
dc.departmentBAİBÜ, Mühendislik Fakültesi, Makine Mühendisliği Bölümü
dc.description.abstractIn this study, the magnetotransport measurements are performed in the field range of 0-7 T to determine the effect of Nd nanoparticles inserted in the Y-123 crystal structure on the superconducting characteristics and flux pinning mechanism of the YBa2-yNdyCu3O7 materials (0.000 a parts per thousand currency sign y a parts per thousand currency sign 0.500). Moreover, the experimental measurement results enable us to evaluate the crucial parameters as regards critical transition temperatures ( and ), room temperature resistivities (rho(300)), residual resistivity ratios (RRR), thermodynamic critical fields (mu H-0(c)), lower critical fields (mu H-0(c1)), upper critical fields (mu H-0(c2)), critical fields (mu H-0(c3)), irreversibility fields (mu H-0(irr)), coherence lengths (xi), penetration depths (lambda) and Ginzburg-Landau () parameters. All the values obtained show the considerable improvement with the increment of the Nd nanoparticles in the Y-123 crystal system up to the critical value of y = 0.250 beyond which the prompt degradation begins in the crystal structure due to new induced artificial dislocations and permanent disorders in the Cu-O-2 consecutively stacked layers. Hence, the excess Nd inclusions lead to the thermal motion of the vortices easily. This fact is completely confirmed by the magnetotransport measurements performed in the external magnetic fields. Namely, the optimum level of Nd dopant seriously increases the coupled regions as a result of the degradation of pancake positional fluctuations, and pinning of two-dimensional pancake vortices enhances with the recoupling of the adjacent layers. However in case of the maximum Nd inclusions, the flattened pancakes with more interplane interaction energy never travel from layer to layer due to the alteration of the coupled vortices into the discrete pancakelike (recoupling linelike) nature. In other words, the excess Nd nanoparticles inserted in the Y-123 crystal system reduce significantly the interlayer Josephson coupling length, elastic moduli of the vortex lattice and magnetic field carrying capacity. Furthermore, the flux pinning energy (U-0) is calculated from thermally activated flux flow model. The activation energy computed increases regularly with the increment of Nd decorations until y = 0.250 after which the value significantly decreases towards to the global minimum point. However, the pinning energy values always decrease with the increase of the external magnetic field strength. In case of external magnetic fields of 7 T the maximum activation energy is found to be about 477 K. As for the Y-123 material doped with maximum Nd additives of y = 0.500, the flux pinning energy values are not calculated at any applied magnetic field which is > 0.1 T due to the cooper pair-breaking in Ba-site Nd substituted Y-123 systems. At the same time, the evaluated parameters follow the same trend: firstly enhancement up to the critical Nd dopant value of y = 0.250 and then the rapid regression towards the global minimum point. Finally, the optimum Nd impurity level is found to be y = 0.250 in the Y-123 system at even higher applied magnetic field strengths.en_US
dc.identifier.doi10.1007/s10854-016-4655-6
dc.identifier.endpage7003en_US
dc.identifier.issn0957-4522
dc.identifier.issn1573-482X
dc.identifier.issue7en_US
dc.identifier.scopus2-s2.0-84961163795en_US
dc.identifier.scopusqualityQ2en_US
dc.identifier.startpage6992en_US
dc.identifier.urihttps://doi.org/10.1007/s10854-016-4655-6
dc.identifier.urihttps://hdl.handle.net/20.500.12491/8770
dc.identifier.volume27en_US
dc.identifier.wosWOS:000377896400049en_US
dc.identifier.wosqualityQ2en_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.indekslendigikaynakScopusen_US
dc.institutionauthorSarıtekin, Namık Kemal
dc.institutionauthorÖz, Muhammed
dc.institutionauthorTerzioğlu, Cabir
dc.institutionauthorGörür, Osman
dc.institutionauthorYıldırım, Gürcan
dc.language.isoenen_US
dc.publisherSpringeren_US
dc.relation.ispartofJournal Of Materials Science-Materials In Electronicsen_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectBa/Nden_US
dc.subjectY-123 Superconductor
dc.subjectNd Nanoparticles
dc.subjectYBa2-yNdyCu3O7
dc.subjectTonset C
dc.subjectToffset C
dc.titleSignificant development on pinning of vortices in Y-123 superconductor with homovalent Ba/Nd substitutionen_US
dc.typeArticleen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim Yok
İsim:
Saritekin2016_Article_SignificantDevelopmentOnPinnin.pdf
Boyut:
1.18 MB
Biçim:
Adobe Portable Document Format
Açıklama:
Tam Metin/Full Text
İndir

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Fizik Bölümü Koleksiyonu
Kimya ve Kimyasal İşleme Teknolojileri Bölümü
Makine Mühendisliği Bölümü Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu