Effects of nickel coating of mold plates on star crack defects

Basit Öğe Kaydı
dc.authorid0000-0002-5820-1871en_US
dc.authorid0000-0002-1377-9338en_US
dc.contributor.authorÖztürk, Sabri
dc.contributor.authorArıkan, Mustafa Merih
dc.contributor.authorKaçar, Yılmaz
dc.date.accessioned2021-06-23T19:34:33Z
dc.date.available2021-06-23T19:34:33Z
dc.date.issued2013
dc.departmentBAİBÜ, Mühendislik Fakültesi, Makine Mühendisliği Bölümüen_US
dc.description.abstractStar crack defects encountered during the continuous casting of slab are elucidated in the current article. Trials were carried out to obtain basic information on the behavior of the star cracks under same casting conditions for different grade materials. It is important that star cracks form in the mold, and increase later in the casting process during the straightening. Star crack defects are clearly seen when using copper-based molds. The influences of steel carbon content, material grades, and mold type have been discussed. It is believed that defects in continuously cast products are minimized while using a nickel-coated mold wall in casting.en_US
dc.identifier.doi10.1007/s11663-013-9821-0
dc.identifier.endpage710en_US
dc.identifier.issn1073-5615
dc.identifier.issn1543-1916
dc.identifier.issue3en_US
dc.identifier.scopus2-s2.0-84877743824en_US
dc.identifier.scopusqualityQ1en_US
dc.identifier.startpage706en_US
dc.identifier.urihttps://doi.org/10.1007/s11663-013-9821-0
dc.identifier.urihttps://hdl.handle.net/20.500.12491/7549
dc.identifier.volume44en_US
dc.identifier.wosWOS:000318736900019en_US
dc.identifier.wosqualityQ2en_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.indekslendigikaynakScopusen_US
dc.institutionauthorÖztürk, Sabri
dc.language.isoenen_US
dc.publisherSpringeren_US
dc.relation.ispartofMetallurgical And Materials Transactions B-Process Metallurgy And Materials Processing Scienceen_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.titleEffects of nickel coating of mold plates on star crack defectsen_US
dc.typeArticleen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim Yok
İsim:
sabri-ozturk.pdf
Boyut:
532.22 KB
Biçim:
Adobe Portable Document Format
Açıklama:
Tam metin/Full text
İndir

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Makine Mühendisliği Bölümü Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu