Fabrication of nano-crystalline undoped and some lanthanide ions (Eu³? and Sm³?) doped calcium pyroborate ceramic powders.

Basit Öğe Kaydı
dc.contributor.advisorMorkan, Ayşe
dc.contributor.authorKemer, Seda Ayten
dc.date.accessioned2024-09-27T21:34:49Z
dc.date.available2024-09-27T21:34:49Z
dc.date.issued2024
dc.departmentBAİBÜ, Lisansüstü Eğitim Enstitüsü, Kimya Ana Bilim Dalıen_US
dc.descriptionLisansüstü Eğitim Enstitüsü, Kimya Ana Bilim Dalıen_US
dc.description.abstractBu çalışmada, nano-kristalin katkısız ve bazı lantanit iyonu (Eu³? and Sm³?) katkılı kalsiyum piroborat seramik tozların üretimi, başlangıç malzemeleri, kalsiyum nitrat ve borik asit, nadir toprak metalleri ve çeşitli yakıtlar (üre, tartarik asit, glisin, sitrik asit, HMTA) kullanılarak çözeltide yanma sentezi (SCS) yöntemiyle başarıyla sentezlendi. Nadir toprak metallerinin farklı konsantrasyonları olarak; Eu³?(0,005, 0,01, 0,02, 0,05) ve Sm³?(0,005, 0,01, 0,015) uygulandı. Ürünler, X-Işını Kırınımı (XRD) ve Kızılötesi spektroskopisi (FTIR) kullanılarak karakterize edildi. Çeşitli yakıt kaynaklarının ve değişen sıcaklık aralıklarının (400-900C°) sentezlenen ürünlerin yapısal özelliklerine etkisi XRD tekniği kullanılarak analiz edilmiş ve bor-oksijen bağının etkisini belirlemek için FT-IR analizi yapılmıştır. Verilere dayanarak, 900°C'de tek fazlı alfa formunda katkısız ve bazı lantanit iyonu (Eu? and Sm³?) katkılı kalsiyum piroboratların, monoklinik kristal yapısıyla oluştuğu belirlendi. FT-IR verilerinin belirlenmesiyle, kalsiyum piroboratların bağ değişikliği, üçgen [BO?]3? yapısının B–O germe modlarına atfedilen >1000 cm?1 civarında gözlendi. Ayrıca 600 ila 820 cm?1 arasındaki bantların, BO? gruplarının B-O bağının bükülme titreşiminden kaynaklandığı saptandı.en_US
dc.description.abstractIn this study, nano-crystalline undoped and some lanthanide ion (Eu? and Sm³?) doped calcium pyroborate ceramic powders production were successfully synthesized by solution combustion synthesis (SCS) method using calcium nitrate, boric acid, rare earth metals, and several fuels (urea, tartaric acid, glycine, citric acid and HMTA) as starting materials. Different concentrations of rare earth metals were applied such as Eu³? (0.005, 0.01, 0.02, 0.05) and Sm³?(0.005, 0.01, 0.015). The characterization processes of products were analyzed using X-Ray Diffraction (XRD) and Infrared spectroscopy (FTIR). The impact of several fuel resources and annealing temperatures (400-900 °C) on the structural features of the synthesized products was examined by the XRD technique. Based on the XRD data, it was found that the single-phase alpha forms of undoped and lanthanide ion doped calcium pyroborates were fabricated at 900 °C with monoclinic crystal structure. Examining the FT-IR spectra, the bond variation of calcium pyroborates were observed at >1000 cm?1 assigned to the B–O stretching modes of the triangular [BO?]3? . It was also determined that the bands betweeen 600 to 820 cm?1 originated from the bending vibrational motions of B-O bond of BO? groups.en_US
dc.identifier.endpage82en_US
dc.identifier.startpage1en_US
dc.identifier.urihttps://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=weFMBHaUra8rsS5wi2bmHH6RrCW_ms8wX9OUUMOqd1GgNFP7CZeIK5MCUE5zd8dp
dc.identifier.urihttps://hdl.handle.net/20.500.12491/20890
dc.identifier.yoktezid849038en_US
dc.language.isoenen_US
dc.publisherBolu Abant İzzet Baysal Üniversitesien_US
dc.relation.publicationcategoryTezen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.subjectKimyaen_US
dc.subjectChemistryen_US
dc.titleFabrication of nano-crystalline undoped and some lanthanide ions (Eu³? and Sm³?) doped calcium pyroborate ceramic powders.en_US
dc.typeMaster Thesisen_US