Yavuz, TevfikÖzyılmaz, Özgün YusufÖztürk, Atiye NilgünAykent, Filiz2021-06-232021-06-2320161119-3077https://doi.org/10.4103/1119-3077.178909https://hdl.handle.net/20.500.12491/8631Objectives: This study evaluated the microtensile bond strength (mu TBS) of a resin composite bonded to bleached enamel as a function of bleaching conditions. Materials and Methods: The whiteness hydrogen peroxide (HP) bleaching agent containing 35% HP was applied to the central incisors' facial enamel surface and irradiated as follows: No treatment (G1; control); no light (G2); light-emitting diode, the 40s (G3); diode laser, the 20s (G4); and neodymium: yttrium aluminum garnet laser, 20s (G5). A Variolink II resin composite structure was then built up incrementally on the surface. The teeth were sectioned into three 1.2 mm x 1.2 mm wide "I"-shaped sections. The specimens were then subjected to microtensile testing at a crosshead speed of 1 mm/min. Data were analyzed using one-way ANOVA (alpha = 0.05) followed by the Tukey Honestly Significant Difference post-hoc test. The fractured surfaces were observed with a stereomicroscope at x 100 magnification. Results: One-way ANOVA revealed no statistical differences among the groups (P > 0.05). No differences appeared between the groups bonded 14 days after bleaching (P > 0.05). Mean mu TBS values (MPa) were as follows: 22.05 +/- 5.01 (G1); 19.6 +/- 5.6 (G2); 19.3 +/- 5.4 (G3); 20.08 +/- 2.08 (G4); and 18.1 +/- 4.8 (G5). Many adhesive failures occurred at the bleached and irradiated enamel surfaces. Conclusion: The various irradiation treatments following the application of the whiteness HP bleaching agent to enamel did not significantly reduce the mu TBS within a 14-day period.eninfo:eu-repo/semantics/closedAccessBleaching AgentsLasersLasers Neodymium: Yttrium Aluminum GarnetResin BondingTooth BleachingArticle10.4103/1119-3077.178909196766771278114492-s2.0-84996484099Q3WOS:000391532500014Q4