Yılmaz, SerdarTürkoğlu, OrhanArı, MusabBelenli, İbrahim2021-06-232021-06-2320110366-6913https://doi.org/10.1590/S0366-69132011000200009https://hdl.handle.net/20.500.12491/5105Electrical conductivity of tetragonal ?-phase (Bi2O 3)1-x(Eu2O3)x (0.01 ? × ? 0.10 %mol) ceramic systems were investigated. The temperature and doping concentration dependences of the electrical conductivity were studied by four-point probe technique. The electrical conductivity increases with the increasing doping concentration and temperature. The highest value of the electrical conductivity is 0.013 ?-1cm-1 (x = 0.05, 750 °C) for the ?-phase at 670 oC and 0.57 ?-1cm -1 (x=0.05, 800 °C) in binary systems at 690 °C. The phase transition which manifests itself by the jump in the conductivity curves was seen and verified by differential thermal analysis measurements. The activation energies of the samples were found to be about 0.71-1.57 eV.Foi estudada a condutividade elétrica de sistema cerâmicos da fase β tetragonal (Bi2 O3 )1-x(Eu2 O3 )x (0,01 ≤ x ≤ 0,10 mol%). A dependência da condutividade elétrica da temperatura e da concentração de dopantes foi estudada pela técnica das quatro pontas de prova. A condutividade elétrica aumenta com o aumento da concentração de dopantes e da temperatura. O maior valor da condutividade elétrica é 0,013 Ω-1cm-1 (x = 0,05, 750 o C) para a fase β a 670 o C e 0,57 Ω-1cm-1 (x = 0,05, 800 o C) em sistema binários a 690 o C. A transição de fase que se verifica pelo salto nas curvas de condutividade elétrica foi confirmada por medidas de análise térmica diferencial. As energias de ativação para as várias amostras está na faixa 0,71-1,57 eVeninfo:eu-repo/semantics/openAccessAnionic ConductorsBismuth OxideFour-point Probe TechniqueIonic ConductivityCondutores Aniônicos,Oxido de BismutoCondutividade IônicaTécnica Das Quatro Pontas de ProvaArticle10.1590/S0366-69132011000200009573421851922-s2.0-79960639641Q3