Ülgen, Asaf TolgaKaraboğa, FıratKarakaya, MehmetPodila, RamakrishnaRao, Apparao M.Belenli, İbrahim2021-06-232021-06-2320190272-88421873-3956https://doi.org/10.1016/j.ceramint.2018.09.282https://hdl.handle.net/20.500.12491/10231This study investigates the effect of gold nanoparticles (Au-NPs) on structural, morphological, electrical and magnetic properties of Fe/MgB2 wires 1.00 mm in diameter. Au-NPs were obtained by pulsed laser ablation of gold in acetone and mixed with Mg + 2B powder mixture for in-situ powder-in-tube wire making process. Resulting drawn wires were subjected to inert atmosphere heat treatments at different temperatures. Transport measurements were performed on 1.00 mm round wires samples in a closed cycle cryostat under magnetic fields perpendicular to wire axis.eninfo:eu-repo/semantics/closedAccessMgB2/Fe Superconducting WireGold Nano-particlesCritical Current Under Applied Magnetic FieldArticle10.1016/j.ceramint.2018.09.282451103110362-s2.0-85054189015Q1WOS:000452570300129Q1