Effect of rapidly annealing process on MgB2 superconducting wires
Yükleniyor...
Dosyalar
Tarih
2019
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
The present study has reported the effect of rapidly annealing and cooling process on the transport and morphological properties of Fe/MgB2 wires. Transport properties like critical transition temperature, transition width and engineering critical current density of the obtained wires at different annealing and durations were determined for superconducting wires. The results show that the annealing temperature is more dominant to accelerate the reaction rate of Mg and B in the wires in comparison with annealing duration. Among the studied wires, a highest Jc (T = 36K) value >150 A/cm2 was achieved for the wires at 900oC and 1000oC for small durations (15 minutes). In the study, it was investigated whether fast annealing and cooling is a possible candidate to fabricate fast the requested superconducting MgB2 long length wires for coils by React&Wind method in continuous system or not.
Açıklama
Anahtar Kelimeler
MgB2 Wire, Critical Current Density, Heat Treatment
Kaynak
Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi
WoS Q Değeri
Scopus Q Değeri
Cilt
23
Sayı
5