Evaluation of the shear bond strength of various adhesive systems to calcium silicate based pulp capping materials
Küçük Resim Yok
Tarih
2023
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Aim: This study aimed to evaluate the shear bond strength (SBS) values of different adhesive systems to calcium silicate and calcium hydroxide-based pulp capping materials. Methods: Cylinder-shaped cavities (2x5 mm) were prepared in the middle of 120 acrylic blocks. Three pulp capping materials (Biodentine, TheraCal LC, Kerr Life) were placed into the cavities. Single Bond 2 (SB2), Clearfil SE Bond (CSB), Clearfil Universal Bond (CUB), Tokuyama Self-cured Universal Bond (TUB) were applied for each pulp capping material (n=10). After composite resin cylinders were prepared, SBS tests were carried out. Data and failure modes were analyzed using two-way ANOVA, Tamhane’s T2 (p?0.05), and stereomicroscope, respectively. Results: TheraCal LC showed the highest SBS values, and there was a statistically significant difference amongst pulp capping materials for all adhesives (p?0.05). The lowest results were found in the Life+TUB (0.79±0.14), and the highest was TheraCal LC+CSB (8.55±1.73). In Biodentine, all adhesive systems showed lower results than TheraCal LC groups, whereas there was a statistically significant difference between SB2 and TUB compared to the Life. Conclusion: TheraCal LC, which has the highest bond strength value in different generation adhesive systems, can be preferred as a pulp capping agent for composite restorations.
Açıklama
Anahtar Kelimeler
Biodentine, calcium hydroxide, calcium silicate, dental adhesives, pulp capping
Kaynak
ANADOLU KLİNİĞİ TIP BİLİMLERİ DERGİSİ
WoS Q Değeri
Scopus Q Değeri
Cilt
28
Sayı
3