Solid particle erosion and scratch behavior of novel scrap carbon fiber/glass fabric/polyamide 6.6 hybrid composites

Yükleniyor...
Küçük Resim

Tarih

2023

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

Wiley

Erişim Hakkı

info:eu-repo/semantics/openAccess

Özet

This study investigated the tribological performance of hybrid composites composed of scrap carbon fiber (CF), glass fabric (GF), and polyamide 6.6 (PA6.6) through an innovative approach for reusing scrap CFs in high-value composite structures. The experimental setup included CF/GF/PA6.6 hybrid composite laminates with varying CF contents and surface-modified GFs, as well as PA6.6 sheets and GF/PA6.6 composite laminates. Solid particle erosion and scratch tests were conducted to assess the influence of scrap CF hybridization and GF surface modification on the tribological properties of the composites. The results demonstrated that neat PA6.6 sheets exhibited the lowest erosion rate, while the incorporation of CF and GF reinforcements had a detrimental effect on erosion resistance. The highest erosion rate was observed within the impact angle range of 15 degrees -30 degrees for pure PA6.6 sheets, whereas for composite laminates, it occurred within the range of 30 degrees-45 degrees. In contrast, CFs positively affected scratch hardness despite their negative impact on erosion resistance. Additionally, the silane treatment of GFs, which enhanced interfacial strength, improved the erosion resistance and scratch hardness of GF/PA6.6 composite laminates without CF. Profilometer-based topographic analysis revealed a correlation between the average surface roughness of the eroded surfaces and the weight loss resulting from solid particle erosion.

Açıklama

Anahtar Kelimeler

Polymer Matrix Composites, Scrap Carbon Fiber, Silane Treatment, Surface Analysis, Wear, Damage

Kaynak

Polymer Composites

WoS Q Değeri

Q1

Scopus Q Değeri

Q1

Cilt

44

Sayı

10

Künye

Kocoglu, H., Korkusuz, O. B., Ozzaim, P., Kodal, M., Altan, M. C., Sinmazcelik, T., ... & Ozkoc, G. (2023). Solid particle erosion and scratch behavior of novel scrap carbon fiber/glass fabric/polyamide 6.6 hybrid composites. Polymer Composites, 44(10), 7197-7211.